Dynaflex D3202-1000-03 TPE

Dynaflex D3204-1000-03 TPE

Dynaflex D3226-1000-03 TPE

Dynaflex G2701-1000-02 TPE

Dynaflex G2701C TPE

Dynaflex G2703-1000-00 TPE

Dynaflex G2706-1000-00 TPE

Dynaflex G2709-1000-00 TPE

Dynaflex G2711-1000-00 TPE

Dynaflex G2712-1000-02 TPE

Dynaflex G2730 TPE

Dynaflex G2745 TPE

Dynaflex G2755-1000-00 TPE

Dynaflex G2755C TPE

Dynaflex G2780-0001 TPE

Dynaflex G6703-0001 TPE

Dynaflex G6713-0001 TPE

Dynaflex G6713C GLS TPE

Dynaflex G7410-1000-00 TPE

Dynaflex G7430-9001-00 TPE

Dynaflex G7431-1001-00 TPE

Dynaflex G7630-1 TPE

Dynaflex G7630-9 TPE

Dynaflex G7640-1 TPE

Dynaflex G7640-9 TPE

Dynaflex G7650-1 TPE

Dynaflex G7650-9 TPE

Dynaflex G7660-1 TPE

Dynaflex G7660-9 TPE

Dynaflex G7670-1 TPE

Dynaflex G7670-9 TPE

Dynaflex G7680-1 TPE

Dynaflex G7680-9 TPE

Dynaflex G7690-1 TPE

Dynaflex G7690-9 TPE

Dynaflex G7702-9001-02 TPE

Dynaflex G7736-1 GLS TPE

Dynaflex G7930-1001-00 GLS TPE

Dynaflex G7930-9001-02 GLS TPE

Dynaflex G7940-1001-00 GLS TPE

Dynaflex G7940-9001-02 GLS TPE

Dynaflex G7950-1001-00 GLS TPE

Dynaflex G7950-9001-02 GLS TPE

Dynaflex G7960-1001-00 GLS TPE

Dynaflex G7960-9001-02 GLS TPE

Dynaflex G7970-1001-00 GLS TPE

Dynaflex G7970-9001-02 GLS TPE

Dynaflex G7980-1001-00 GLS TPE

Dynaflex G7980-9001-02 GLS TPE

Dynalloy 8900-30 TPE

Dynalloy 8900-60 TPE

Dynalloy 8900-80 TPE

Dynalloy OBC 8100-N50 TPE

Dynalloy OBC 8100-N65 TPE

Dynalloy OBC 8100-N75 TPE

Dynalloy OBC8000-B30 TPE

Dynalloy OBC8000-N30 TPE

Dynalloy OBC8000-T05 TPE

Dynalloy OBC8000-T40 TPE

Dynalloy OBC8000-T60 TPE

Dynalloy OBC8200-BT50 TPE

Dynaflex G2780-0001 物性表

基本信息
特性	抗紫外线性能良好 可回收材料 良好的着色性 耐臭氧性能
用途	包覆成型 吹塑成型应用 个人护理 片材 透明或半透明配件 消费品应用领域
机构评级	FDA 21 CFR 177.26002
RoHS 合规性	RoHS 合规
外观	半透明
形式	粒子
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
比重	0.898	g/cm3	ASTM D792
熔流率（熔体流动速率）			ASTM D1238
190°C/2.16 kg	5.0	g/10 min	ASTM D1238
200°C/5.0 kg	16	g/10 min	ASTM D1238
收缩率 - 流动	0.90 到 1.5	%	ASTM D955

硬度	额定值	单位制	测试方法
肖氏硬度(邵氏 A, 10 秒)	84		ASTM D2240

弹性体	额定值	单位制	测试方法
拉伸应力1			ASTM D412
100%应变, 23°C2	5.79	MPa	ASTM D412
300%应变, 23°C3	7.86	MPa	ASTM D412
抗张强度(断裂, 23°C)	7.58	MPa	ASTM D412
伸长率(断裂, 23°C)	350	%	ASTM D412
撕裂强度	43.8	kN/m	ASTM D624
压缩永久变形(23°C, 22 hr)	18	%	ASTM D395B

充模分析	额定值	单位制	测试方法
表观粘度(200°C, 11200 sec^-1)	22.0	Pa·s	ASTM D3835

补充信息

Dynaflex G2780-0001 can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.Municipality waste stream recycle code is "7" which is designated for "Other".Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.

注射	额定值	单位制
建议的最大回制料比例	20	%
料筒后部温度	132 到 171	°C
料筒中部温度	171 到 188	°C
料筒前部温度	188 到 207	°C
射嘴温度	188 到 207	°C
模具温度	15.6 到 26.7	°C
背压	0.00 到 1.03	MPa
螺杆转速	40 到 100	rpm

注射说明

以聚丙烯 (PP)、乙烯醋酸乙烯共聚物 (EVA) 或低密度聚乙烯 (PE) 为基础的色母料最适合 Dynaflex G2780-0001 着色。使用熔体流动速率较高（范围为 25 - 40 克/10 分钟）的色母料，则能达到较好的颜色分散效果。典型的色母料用量为 1% 至 5%（重量）。可以使用液体颜料，但以矿物油为基础的载体对最终硬度值会有显著的影响。不应采用以 PVC 为基础的色母料。若使用 GLS 可供的预着色复合材料，则可达到较好的配色一致性。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Dynaflex? G2780-0001 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Dynaflex? G2780-0001 具有极好的熔体稳定性。最长停留时间可能会根据机筒尺寸有所变化。通常，如果机器闲置 8 - 10 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：100 - 500 psi第二阶段 - 保持压力：70% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒

备注
1 .	2 小时
2 .	口模 C
3 .	C 模具