1.41 g/cm3
23 °C
ISO 1183
0.70 g/cm3
ISO 60
0.090 %
2 mm
60x60x2mm
120 °C
4 hr
ISO 294-4
1.1 %
600 bar
2 mm
60x60x2mm
290 °C
80 °C MT
ISO 294-4
0.050 %
2 mm
60x60x2mm
120 °C
4 hr
ISO 294-4
0.37 %
600 bar
2 mm
60x60x2mm
290 °C
80 °C MT
ISO 294-4
5.0 %
23 °C
ISO 62
1.8 %
50% RH
23 °C
ISO 62
10300 MPa
23 °C
ASTM D638
6790 MPa
23 °C
ASTM D638
11200 MPa
23 °C
ISO 527-2/1
7500 MPa
23 °C
ISO 527-2/1
179 MPa
23 °C
ASTM D638
125 MPa
23 °C
ASTM D638
200 MPa
23 °C
ISO 527-2/5
135 MPa
23 °C
ISO 527-2/5
3.0 %
23 °C
ASTM D638
6.0 %
23 °C
ASTM D638
3.0 %
23 °C
ISO 527-2/5
5.0 %
23 °C
ISO 527-2/5
7000 MPa
1 hr
ISO 899-1
5800 MPa
1000 hr
ISO 899-1
8400 MPa
23 °C
ASTM D790
5900 MPa
23 °C
ASTM D790
10500 MPa
2 mm/min
23 °C
ISO 178/A
7000 MPa
2 mm/min
23 °C
ISO 178/A
290 MPa
23 °C
ASTM D790
200 MPa
23 °C
ASTM D790
300 MPa
2 mm/min
23 °C
ISO 178/A
220 MPa
2 mm/min
23 °C
ISO 178/A
280 MPa
2 mm/min
3.5% Strain
23 °C
ISO 178/A
170 MPa
2 mm/min
3.5% Strain
23 °C
ISO 178/A
4.0 %
2 mm/min
23 °C
ISO 178/A
6.0 %
2 mm/min
23 °C
ISO 178/A
10 kJ/m2
-30 °C
ISO 179/1eA
10 kJ/m2
-30 °C
ISO 179/1eA
12 kJ/m2
23 °C
ISO 179/1eA
20 kJ/m2
23 °C
ISO 179/1eA
70 kJ/m2
-30 °C
ISO 179/1eU
75 kJ/m2
-30 °C
ISO 179/1eU
85 kJ/m2
23 °C
ISO 179/1eU
90 kJ/m2
23 °C
ISO 179/1eU
10 kJ/m2
-30 °C
ISO 180/1A
10 kJ/m2
-30 °C
ISO 180/1A
12 kJ/m2
23 °C
ISO 180/1A
15 kJ/m2
23 °C
ISO 180/1A
70 kJ/m2
-30 °C
ISO 180/1U
80 kJ/m2
23 °C
ISO 180/1U
2.80 J
-30 °C
ISO 6603-2
3.90 J
23 °C
ISO 6603-2
900 N
-30 °C
ISO 6603-2
1030 N
23 °C
ISO 6603-2
250 °C
0.45 MPa
ISO 75-2/B
250 °C
1.8 MPa
ISO 75-2/A
230 °C
ISO 306/B50
ISO 306/B120
263 °C
10 °C
min
ISO 11357-3
2.0E-5 cm/cm/°C
23 - 55 °C
ISO 11359-2
1.0E-4 cm/cm/°C
23 - 55 °C
ISO 11359-2
HB
0.75 mm
UL 94
HB
1.5 mm
UL 94
600 °C
2 mm
IEC 60695-2-12
23 %
ISO 4589-2
passed
1 mm
ISO 3795
1.0E+15 ohms
IEC 60093
1.0e+15 ohms·cm
23 °C
IEC 60093
39 kV/mm
23 °C
1 mm
IEC 60243-1
5.00
100 Hz
23 °C
IEC 60250
4.00
23 °C
1 MHz
IEC 60250
0.030
100 Hz
23 °C
IEC 60250
0.027
23 °C
1 MHz
IEC 60250
600 V
IEC 60112