PVDF/705/Arkema Technical Polymers 物性表
PVDF/705/Arkema Technical Polymers
规格用途
该料用途 | 电线电缆应用; 涂层应用; 细丝 |
备注说明 | Kynar® resins are fluorinated thermoplastic homopolymers.Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties.Main applications: corrosion protection in the chemical industry, coating (painting, co-extrusion), off shore, wire and cable.Kynar® 705 resin is a grade of granules for injection molding, rotomolding applications and multifilament extrusion. |
技术参数
性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
注射 | 加工(熔体)温度 | ꔲ沈 到 팒푰 | °C | 模具温度 | 팒 到 沈 | °C |
物理性能 | 密度 | ISO 1183 | ꔲ.푰 | g/cm³ | 熔融体积流量(MVR) | ISO 1133 | 230°C/5.0 kg | . | cm³/10min | 收缩率 | ISO 294-4 | 横向流量 | 팒. | % | 流量 | 팒. | % | 吸水率 | ISO 62 | 饱和, 23°C | .팒 | % |
热性能 | 热变形温度 | ISO 75-2/A | 1.8 MPa, 未退火 | ꔲꔲ팒 | °C | 玻璃转化温度 2 | ISO 11357-2 | -. | °C | 熔融温度 2 | ISO 11357-3 | ꔲ푰 | °C | 线形热膨胀系数 | ISO 11359-2 | 流动 : -40 到 100°C | ꔲ.혒- | cm/cm/°C | 横向 : -40 到 100°C | ꔲ.혒- | cm/cm/°C |
可燃性 | 可燃性等级 | IEC 60695-11-10, -20 | 1.5 mm | 읅- | 极限氧指数 | ISO 4589-2 | | % |
充模分析 | 熔体导热性 | .ꔲ沈 | W/m/K | ||
机械性能 | 拉伸模量 | ISO 527-2 | 팒 | MPa | 拉伸应力 | ISO 527-2 | 屈服 | 혒. | MPa | 拉伸应变 | ISO 527-2 | 屈服 | . | % | 标称拉伸断裂应变 | ISO 527-2 | > 혒 | % |
冲击性能 | 简支梁缺口冲击强度 | ISO 179/1eA | 23°C | 륇. | kJ/m² | 简支梁无缺口冲击强度 | ISO 179/1eU | 23°C | 팒 | kJ/m² |
温馨提示:此数据表中的信息由塑胶网从该材料的生产商处获得,塑胶网尽最大努力确保此数据的准确性,但是塑胶网对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。